Selection Guide - we are able to create a wide variety of waxes in commercial quantities for every type of candle.

download Lipidchem wallpaper & screensaver. click here.

Code No. Description Application Remarks Palm Wax 5801A Specially blended Palm Wax with Slip Melt Point of 58 - 65°c and manufactured into a physical form of granular beads. Suitable for pillars of 2 inches diameter and above. Crystal formation : Large It can be used as an outer case if pillars are made with an innercore. Pouring temperature around 93 - 95°c. Needs constant stirring to remove air trap during crystallization. Aluminium moulds give best crystal formation. Other mould need tempering to obtain same results. Palm Wax 5701A Specially blended Palm Wax with Slip Melt Point of 55 - 60°c and manufactured into a physical form of granular beads Suitable for pillars of 2 inches diameter and above. Crystal formation : Medium It can be used as an outer case if pillars are made with an innercore. Pouring temperature around 93 - 95°c. Needs constant stirring to remove air trap during crystallization. Aluminium moulds give best crystal formation. Other mould need tempering to obtain same results. Palm Wax 5601A Specially blended Palm Wax with Slip Melt Point of 56 - 62°c and manufactured into a physical form of granular beads. Suitable for pillars of 2 inches diameter and above. Crystal formation : Medium It can be used as an outer case if pillars are made with an innercore. Pouring temperature around 93 - 95°c. Needs constant stirring to remove air trap during crystallization. Aluminium moulds give best crystal formation. Other mould need tempering to obtain same results. Palm Wax 5501A Specially blended Palm Wax with Slip Melt Point of 52 - 58°c and manufactured into a physical form of granular beads Suitable for pillars of 2 inches diameter and above. Crystal formation : Fine It can be used as an outer case if pillars are made with an innercore. Pouring temperature around 93 - 95°c. Needs constant stirring to remove air trap during crystallization. Aluminium moulds give best crystal formation. Other mould need tempering to obtain same results. Palm Wax 5401A Specially blended Palm Wax with Slip Melt Point of 52 - 55°c and manufactured into a physical form of granular beads. Suitable for containers. Crystal formation : Fine and Uniform when poured at high temperature 95'c. No crystals when poured below 65°c. Needs constant stirring to remove air trap during crystallization. Shrinkage is minimum. Palm Wax 1301A Specially blended Palm Wax with Slip Melt Point of 58°c and manufactured into a physical form of granular beads. Suitable for Tea Lights, Votives and inner core. Crystal formation : Plain Pouring temperature around 60 - 65°c Needs constant stirring to remove air trap during crystallization. Palm Wax 1701A Specially blended Palm Wax with Slip Melt Point of 54 - 57°c and manufactured into a physical form of granular beads. Suitable for Tapers and Chandelier Candles with use of suitable wicks. Crystal formation : Plain Pouring temperature around 85 - 90°c. Needs constant stirring to remove air trap during crystallization. Palm Wax 1601A A softer grade of Palm Wax. It would therefore take the physical form of blocks following the size of the 20 kg cartons. Not suitable for making candles by itself but a very reliable wax for blending with other waxes for making many types of candles Crystal formation : Plain When blended with paraffin pouring temperature is around 90°c. Needs constant stirring to remove air trap during crystallization.